昆明鋁單板幕墻施工找正規廠家非常重要,云南亞太鋁業有限公司多年來從事昆明鋁單板幕墻安裝施工,下面給大家介紹昆明幕墻氟碳鋁單板安裝施工的標準:
物理性規格 | 試驗項目TESTITEMS | AAMA2605規范(98) AAMA2605SPEC(98) | 結果RESULT | 備注 REMAKES |
光(guang)澤度(60°) (Gloss--60°) | 低(di)規格:最低(di)19,中(zhong)等20-79 高(gao)規格:最高(gao)80Low:Max19. Medium:20-79Hight Min80 | 25-35 | ASTM D52360度光澤(ze)測量儀 ASTM D523 (60 degree gloss meter) | |
硬(ying)度(60°)(Dry Film Hardness) | 最低F FMin | H | ASTM D3363海(hai)鷗綠(lv)松石鉛筆 ASTM D3363 (Eagle Tuqouise Pencil) | |
附(fu)著力(Adhesion) | 無剝離(100/100) No Removal Film(100/100) | 100/100 | 切割間(jian)隔1毫米濕(shi)或干膜(mo)Imm Cross Cut Wet&Dry | |
耐沸水性(boiling water resistance) | 無(wu)脫落(100/100) No Removal Film(100/100) | 100/100 | 切割間(jian)隔1毫米99-100℃×20分 1mm Cross Cut Wet&Dry99-100℃×20mins | |
耐沖擊性(Impact Resistance) | 無脫(tuo)落 No Removal Film | 無脫落 No Removal Film | 直徑16毫米,加德(de)納(Gardner)撞擊(ji)試(shi)驗 16mm Corss Gardner impact tester | |
耐磨損性(Abrasion Resistance) | 損耗系數(V/T)_40分鐘 Abrasion Coeffcient value(Y/T)40Min | 65分鐘 | ASTM D968 | |
耐酸(suan)性(Acid Resistance) | 無氣泡無變化(hua)No Blister -ing. No Visual Change | 無(wu)氣泡無(wu)變化No Blistering No Visual Change | 在18-27℃點滴15分鐘實驗(10%鹽酸) 15min(18-27")Spot Test (10%Muriaticacid) | |
耐(nai)砂(sha)漿性(Mortar Resistance) | 漆膜無損(sun)失 無變化No loss of Film Adhesion. No Visual Change | 漆膜(mo)無損失(shi) 無變(bian)化No loss of Film Adhesion. No Visual Change | 24小時輕拍(pai)實驗(yan)24Hrs Pat Test | |
耐(nai)硝酸性(xing)(Nitric Acid Resistance) | 色差最(zui)大為(wei):5 ?EASTMD 2244 Color Change 5AEAS -TMD2244(Hunter)Max | 3?E | 用70%的石(shi)硝酸,30分鐘 70%Nitric Acid 30Mins | |
耐清洗性(Deterent Resistance) | 無氣(qi)泡無變(bian)化ASTM3359 No Blistering No Visua Change ASTM3359 | 無氣泡(pao)無變化No Blistering. No Visual Change | 玻璃清洗劑Glass Cieaner Dropping | |
耐玻璃清(qing)晰(xi)性(xing)(Deter-ent Glass Resistance | 無(wu)氣(qi)泡無(wu)變化No Blistering. No Visual Change | 無(wu)氣(qi)泡無(wu)變化No Blistering. No Visual Change | 3%清洗劑38℃x72小時 3%Detergent.38%x72hrs | |
耐濕性(xing)(Humidity Resistance) | 生銹最大N0.8ASTM- D7714Rusting most N0.8ASTMD714 | 無氣泡 No Blistering | ASTM D2247(100%RH;100°F,4000Hhs) | |
耐(nai)鹽霧性(Salt Spary Resistance) | 受(shou)蝕最大1/32”ASTM -11654Corroded most 1/32"ASTMD714 | 1/32" | ASTM BI117(5% 鹽水,100°F,4000小時) ASTMBI17(S%Salt, 100° F,4000 Hhs) | |
耐(nai)候性(Weathering -color Relention) | 色差最(zui)大為5?EASTM -D2244曝光率最(zui)低50% (60)ASTMD11654 | 3?E80% | 美國(guo)南(nan)佛(fo)羅里達暴曬實驗10年45° SouthFloridaExposure lOYears 45°.Florida(Latitude27° North) | |
耐(nai)老(lao)化性(Chalk Resistance) | 老化率最(zui)大NO.8(白(bai)顏色 以外顏色)最(zui)大NO.6 (白(bai)色)ASTMD659 | 其他顏(yan)色(se):NO.8白色(se):NO.6Colors: NO. 8 White: NO.6 | ||
而寸侵(qin)蝕性(Resistance To Erosion) | 最大損失為10% Maximallossing: 10% | 5% |